Flexform™ 항공우주 티타늄 산업의 이점
Flexform™ High Pressure Warm Forming 프로세스는 Hot-Forming, Hot Stamping, Super Plastic Forming, SPF, Hot Gas Forming 등 기존 티타늄 성형 방법을 대체하거나 보완할 수 있는 새로운 기술입니다.
50% reduction in production costs
Protection gas may be eliminated, due to the relatively low temperature process. Time for part cleaning after processing is reduced to a minimum, and the need for forming tool maintenance is also greatly reduced due to galling from the titanium blanks. Finally, the energy consumption is also greatly reduced, compared to traditional hot forming methods.
Five times increased throughput
The HPWF process, with less than 5 minutes cycle time, including heating, loading, forming and unloading, can handle multiple tools in one and the same forming cycle, while allowing for very rapid tool changes. Forming at relatively low temperatures enables quick cooling. The new Flexform™ HPWF process has a production capacity of some five times traditional hot-forming processes.
Forming repeatability
The flexibility of the process allows for springback compensation in the die design, hence compensation for material spring back can be implemented into the process, allowing final shape parts to come directly from the process.
High Pressure와 온화한 온도 상에서의 티타늄 Ti6AI-4V 성형성
![webinar_knowledgecenter-4.jpg Formability of titanium Ti6AI-4V at moderate temperature combined with high-pressure webinar](https://c1.webien.cloud/pixel.webp)
![airbus Shaping the Aerospace Titanium industry with Flexform presses](https://c1.webien.cloud/pixel.webp)
브로셔 - Flexform 프레스를 통한 항공우주 티타늄 산업 구축
Flexform™ High Pressure Warm Forming 프로세스는 Hot-Forming, Hot Stamping, Super Plastic Forming, SPF, Hot Gas Forming 등 기존 티타늄 성형 방법을 대체하거나 보완할 수 있는 새로운 기술입니다.
![high-pressure-warm-forming-1.jpg](https://c1.webien.cloud/pixel.webp)
백서 - Ti-6Al-4V 부품의 경제성을 재구성하는 High Pressure Warm Forming
Quintus Technologies가 개발한 혁신적이고 새로운 프로세스인 HPWF(High Pressure Warm Forming)는 지금까지 예외적인 소재의 보다 광범위한 채택을 방해했던 비용의 장벽을 무너뜨렸습니다.
![hpwf-plane-wp1 Formability of Titanium Ti-6Al-4V sheets at moderate temperature combined with high-pressure](https://c1.webien.cloud/pixel.webp)
백서 - High Pressure와 온화한 온도에서의 티타늄 Ti-6Al-4V 시트의 성형성
새로운 성형 기술인 HPWF(High Pressure Warm Forming) 프로세스는 High Pressure와 중간 정도의 온도를 결합하여 항공우주용 티타늄 부품을 위한 보다 빠르고 비용 효율적인 제조 솔루션을 제공합니다.